On the Question of a Phase Change in Zirconium Monocarbide

Leonard N. Grossman

No abstract provided

DOI badge Download BibTeX How to cite Download dataset

Materials
Curve 1
Wavelength, µm: 0.65 Temperature Range, K: 1600 Geometry θ': ~0° Composition (weight percent), Specifications and Remarks: Hot pressed in graphite dies from 325 mesh powder; preheated to 2600 K for 1 hr; measured in vacuum (5 x 10⁻⁴ mm Hg).
Curve 2
Wavelength, µm: 0.65 Temperature Range, K: 1600 Geometry θ': ~0° Composition (weight percent), Specifications and Remarks: Above specimen and conditions measured 7 min after flashing.
Curve 3
Wavelength, µm: 0.65 Temperature Range, K: 1600 Geometry θ': ~0° Composition (weight percent), Specifications and Remarks: Above specimen and conditions except measured 14 min after flashing.
Curve 4
Wavelength, µm: 0.65 Temperature Range, K: 1600 Geometry θ': ~0° Composition (weight percent), Specifications and Remarks: Above specimen and conditions except measured 21 min after flashing.
Curve 5
Wavelength, µm: 0.65 Temperature Range, K: 1600 Geometry θ': ~0° Composition (weight percent), Specifications and Remarks: Above specimen and conditions except measured 35 min after flashing.
Curve 6
Wavelength, µm: 0.65 Temperature Range, K: 1600 Geometry θ': ~0° Composition (weight percent), Specifications and Remarks: Above specimen and conditions except measured 60 min after flashing.
Curve 7
Wavelength, µm: 0.650 Temperature Range, K: 1600 Geometry θ': ~0° Composition (weight percent), Specifications and Remarks: Above specimen and conditions measured 60 min after flashing.
Curve 8
Wavelength, µm: 0.65 Temperature Range, K: 1600 Geometry θ': ~0° Composition (weight percent), Specifications and Remarks: Hot pressed in graphite dies from 325 mesh powder; preheated to 2600 K for 1 hr; measured in vacuum (5 x 10⁻⁴ mm Hg).
Curve 9
Wavelength, µm: 0.65 Temperature Range, K: 1600 Geometry θ': ~0° Composition (weight percent), Specifications and Remarks: Above specimen and conditions measured 7 min after flashing.
Curve 10
Wavelength, µm: 0.65 Temperature Range, K: 1600 Geometry θ': ~0° Composition (weight percent), Specifications and Remarks: Above specimen and conditions except measured 14 min after flashing.
Curve 11
Wavelength, µm: 0.65 Temperature Range, K: 1600 Geometry θ': ~0° Composition (weight percent), Specifications and Remarks: Above specimen and conditions except measured 21 min after flashing.
Curve 12
Wavelength, µm: 0.65 Temperature Range, K: 1600 Geometry θ': ~0° Composition (weight percent), Specifications and Remarks: Above specimen and conditions except measured 35 min after flashing.
Curve 13
Wavelength, µm: 0.65 Temperature Range, K: 1600 Geometry θ': ~0° Composition (weight percent), Specifications and Remarks: Above specimen and conditions except measured 60 min after flashing.
Curve 14
Wavelength, µm: 0.650 Temperature Range, K: 1600 Geometry θ': ~0° Composition (weight percent), Specifications and Remarks: Above specimen and conditions measured 60 min after flashing.